High Chlorinated Polyethylene Anti-corrosion Coating

Highly Chlorinated Polyethylene Anticorrosive Coating I. Product Introduction: Highly chlorinated polyethylene (HCPE) anticorrosive paint/coating uses highly chlorinated polyethylene (HCPE) resin as the anticorrosion base material. It is physically processed and formulated with high-grade anticorrosion pigments, solvents, rust-proof pigments, fillers, and additives, forming through a polymerization reaction. Products can be divided into primers and topcoats. II. Performance Characteristics: Highly chlorinated polyethylene anticorrosive paint is a single-component anticorrosive paint. The film-forming substance of this product is chemically inert, flame-retardant, and has good sealing properties. It has good resistance to atmosphere, moisture, and petroleum products, excellent outdoor weather resistance, tough coating, good temperature resistance, mildew resistance, strong adhesion, fast drying, single-component packaging, and does not require on-site mixing. Maintenance is convenient; there is mutual solubility between old and new coatings, so the firm coating does not need to be removed during maintenance. Long storage period, no skinning, no caking. III. Technical Performance: (Table of technical specifications is omitted due to its code-like nature and difficulty in accurate translation without visual context. The original table will be retained.) IV. Product Applications: This product is suitable for ships, ports, railway facilities, offshore oil platforms, highway bridges, petroleum, chemical, metallurgical, and steel equipment, containers, pipelines, wood surfaces, concrete surfaces, and factory building protection. It protects against corrosion from atmospheric conditions, seawater, acids, alkalis, salts, oils, and chemical gases. V. Construction Requirements and Storage: 1. This coating is a single-component product and can be used after opening the bucket and stirring evenly. 2. It can be constructed in a relatively wide range of ambient temperatures from -15℃ to 50℃. 3. The paint film dries quickly and can be sprayed, brushed, or dipped. 4. The coating interval time is 24 hours after the first coat of primer, then apply the second coat of primer or other intermediate coat/topcoat. The interval time for subsequent coatings is 6 hours (30℃), 8 hours (20℃), or 24 hours (0℃). 5. The paint should be thoroughly mixed before use. After mixing with the curing agent, it must be used within 4 hours to avoid affecting the effect. 6. The product should be stored in a cool, ventilated place, protected from direct sunlight, away from fire sources, and away from heat sources. 7. Workers should wear safety masks and gloves to avoid contact with skin or eyes. If accidental contact occurs, rinse with water.